Carbon vs. Alloy vs. Stainless: Steel Grades You Might Buy in China – QualityInspection.org

Carbon vs. Alloy vs. Stainless: Steel Grades You Might Buy in ChinaCarbon vs. Alloy vs. Stainless: Steel Grades You Might Buy in China

There are basically 3 steel grades (types of steel) that are used when it comes to product manufacturing:

  1. Carbon Steel
  2. Alloy Steel
  3. Stainless Steel

Each of these steel grades is comprised of different amounts of iron and carbon (the basic elements of steel), as well as additional alloys in some cases. Let’s explore these steel types in detail…

Which steel grades to choose?

When selecting the right metal for your job, there are several factors that you need to consider:

  • Hardness– capacity to resist abrasion, but also difficulty in being cut or drilled
  • Strength– the amount of force necessary to deform the metal
  • Toughness– ability to resist stress (and not break)
  • Malleability – the ability of the metal to deform
  • Weldability– ability to be welded (it’s a function of melting point, heat conductivity, etc.)

Download a thorough spreadsheet which explains the popular steel grades in detail here.

Let’s go through the 3 types: carbon, alloy, and carbon:

 

1. Carbon Steel (Low & High Grades)

Carbon Steel (an alloy of steel and carbon) gets corroded but it is hard — the more carbon content, the harder the steel. Low-carbon steel is strong and tough and can be case-hardened if needed. High-carbon steel can be heat treated to make it a lot harder, however, in this condition, it tends to be more brittle and more difficult to work with.

Common applications for carbon steel:

  • Tubes, plates, bolts, signs, furniture, fencing and many other common metal parts are made in low carbon steel (also known as ‘mild steel’).
    most popular low carbon steel gradesmost popular low carbon steel grades
  • Professional kitchen knives, cutting tools in CNC machines, drill bits, saws, masonry nails are all made with high carbon steel. The high hardness gives blades and cutting tools a sharp edge that lasts, however, with this hardness comes brittleness which means products tend to break easier.
    most popular high carbon steel gradesmost popular high carbon steel grades

The disadvantage of high-carbon steel is that it is more expensive and harder to machine than alloys with less carbon. It is appropriate when rust is not a concern and when the product doesn’t need to withstand tensile stress (it doesn’t really bend, and it breaks more easily).

 

 2. Alloy Steel

Alloy Steel (which has additional chemical elements added to improve certain properties) – some of the most common alloying elements are manganese, nickel, chromium, molybdenum, vanadium, silicon, and boron.

The improved properties that alloy steels have over carbon steel are:

  • Strength,
  • Hardness,
  • Toughness,
  • Wear resistance,
  • Corrosion resistance,
  • and hardenability.

Common applications for alloy steels:

  • Construction and architecture where strength, toughness and corrosion resistance are a pre-requisite for the material.
  • Jewellery, household items, cutlery, cook wear are all manufactured from alloy steel.

Steel alloys can be split into two categories, low alloy steels and high alloy steels. Low alloy steels have less than 8% total alloying elements in the composition, these steels have better hardness and resistance to wear over carbon steel but tend to have less tensile strength.

The high alloy steels have more than 8% alloying elements and have better properties than those of the low alloying steels.

 

Watch this video from our sister site, Sofeast, to get a more in-depth explanation about carbon and alloy steels:

 

3. Stainless Steel

Stainless Steel (an alloy of steel and chromium) doesn’t corrode easily, but it is not as hard.

Any product that will be in constant contact with liquids is a good candidate for a steel alloy with high chromium content. Stainless steel is an alloy of steel with a minimum of 10.5% and up to 30% chromium that gives this steel its unique properties.

most popular stainless steel gradesmost popular stainless steel grades

Stainless steel is broken into five categories:

a) Austenitic – Austenitic Stainless Steels are classed as the 200 and 300 series and the alloying elements are basically steel with 18% chromium and 8% nickel and low carbon content. The most common steel produced is the 304 Stainless Steel, commonly used for pipework, mining equipment, food and beverage, kitchenware and architecture.

b) Ferritic – Ferritic Stainless Steels are plain chromium stainless steels where the chromium content can vary between 12% and 18%, these also have a low carbon content, similar to the austenitic range. There are classified as the 400 series. This range of stainless steels are magnetic and have good ductility and corrosion resistance. Typical applications are heat exchangers, automotive fasteners, furnace parts, heater parts.

c) Duplex – Duplex Stainless Steels contain a high level of chromium between 18% and 28% as well as nickel between 4% and 8%. This two-high element level gives a mix of austenitic and ferritic structure, hence the name of duplex stainless steel.

Duplex stainless steel is generally twice as hard as plain austenitic or ferritic stainless steels. They have slightly better toughness and ductility properties than ferritic grades but not as good values when compared to the austenitic grades. Duplex grades have higher strength, good weldability, good toughness, and have high resistance to stress corrosion cracking. Typical applications are hot water tanks, brewing tanks, process plant equipment, swimming pool structures.

d) Martensitic – Martensitic Stainless Steels are plain chromium steels containing between 12% and 18% as well as having a relatively high content of carbon of up to 1.2%. Martensitic grades have better corrosion (not as much as austenitic grades) and wear resistance than other Stainless Steel grades and can be heat treated to achieve high hardness values. These grades are magnetic in the annealed and hardened state. Typical applications include cutlery, cook-wear, surgical and dental instruments, springs, scissors, industrial blades, vehicle stampings, screwdrivers, pliers, and staple guns.

e) Precipitation Hardening – Precipitation Hardening Stainless Steels (PHSS) are chromium and nickel with at least one other alloying element (copper, aluminum, titanium, niobium or molybdenum). PHSS grades provide an optimum combination of both martensitic and austenitic grade properties. Like martensitic grades, they are known for their ability to gain high strength through heat treatment and they also have the corrosion resistance of austenitic stainless steel.

The most well-known precipitation hardening stainless steel is 17-4 PH. The name comes from the additions 17% Chromium and 4% Nickel. It also contains 4% Copper and 0.3% Niobium. 17-4 PH is also known as stainless steels grade 630. Typical applications include dental drills and reamers, aircraft components, shaver heads, surgical needles, and aerospace applications.

 

Again, watch this video from Sofeast to take a deep dive into stainless steels and their various properties:

 

Common stainless steel grades

You can get a chart about these grades, their main attributes, and examples of common applications, by clicking here: Stainless Steel Chart.

The three most common steel grades we encounter in China are:

  • 201 – inexpensive and very common
  • 304 – the most common grade of stainless steel
  • 316 – a more expensive grade, with better resistance to corrosion

 

4. A word about stainless iron

Stainless iron is sometimes used, too. The main difference with this material is that it has less than 0.6%Ni or no Ni element in it, such as 403 (12Cr12). It’s widely used in the chemical and construction industries. Any magnetic iron alloy containing more than 12% chromium having a body-centered cubic structure is also known as stainless iron.

 

Most Common Heat Treatment Processes

Heat treatment is the process of heating and cooling the metal without changing its physical shape. There are different heat treatment processes which when applied to different steels can change the properties of that steel, such as its hardness, toughness and even softening, which are all determined by the change in the steel microstructure.

Hardening – A steel with a sufficient amount of carbon content can be hardened by heating it up and then rapidly quenching it. This process creates an austenite microstructure which can be ferrite, martensite or cementite.

Tempering – This process is carried out on carbon steels that have been hardened in order to reduce the brittleness of the steel. The temperature of tempering will depend upon the desired result for the function of the steel product, the lower the tempering temperature the better the strength and hardness.

Annealing – Annealing steel involves heating up the steel past its critical temperature and then letting it cool down very slowly. This results in the steel becoming more machinable and workable from a forming aspect.

Normalizing – This is a similar process to annealing where the steel is heated and cooled slowly, normally just left to cool in room temperature air. This gives steel a microstructure of ferrite and cementite which has higher strength and hardness but lower ductility properties.

Carburizing – Carburizing is also known as case-hardening which is a process of infusing additional carbon to the surface of low carbon steel and then subjecting it to the hardening process. The outer carbon steel will have higher hardness where the inner core will remain tough.

 

How to test a metal to ensure it is the right grade?

The best is to conduct both physical testing and chemical analysis.

The most common physical tests are:

  • Tensile test (applying tension until failure)
  • Hardness (or durometry) test, which can be done in different ways

Chemical analysis is usually done with an X-ray fluorescence tester.

All this has been explained in this article I posted recently on ChinaImportal: Manufacturing Steel Parts in China: CNC, Die Casting & Steel Grades.

 

This FREE eBook starts from the beginning, discussing whether you need to hire a sourcing agent, and follows the sourcing process right through to developing a trusted supplier’s quality and productivity.

There are 15 chapters over 80+ pages to explore, providing exhaustive guidance on the entire sourcing and supplier development process from start to finish, including:

  • Identifying suppliers,
  • Negotiations,
  • Quality inspections,
  • Developing Chinese suppliers,
  • Improving factory quality and productivity,
  • and much more…